Lincoln ED022010 Wearshield 60 Stick SMAW Welding Rod 1/8 14in 4 10 lb Plastic Tubes

SKU: ED022010
$139.83 $157.30
Financing / Leasing Available

Welding Equipment & Industrial Supply Financing

WeldingMart has partnered with Clicklease to offer fast, flexible financing for welding equipment and industrial supplies. Get the equipment you need with affordable monthly payments tailored to your budget.

Whether you're purchasing a new MIG welder, TIG welder, engine-driven welder, or welding accessories, our financing solutions help you equip your shop without large upfront costs. We offer lease-to-own options on trusted brands like Lincoln Electric, Miller Electric, and more.

Apply in minutes and get a decision in seconds:

  • No hard credit check
  • No lengthy paperwork
  • Fast approvals

Why Choose Lease-to-Own Welding Equipment?

Lease-to-own financing gives you the flexibility to grow your business while preserving cash flow.

Key benefits include:

  • Low upfront cost – Start using equipment without a large initial investment
  • Flexible terms – Choose payment plans that fit your budget
  • Access to latest technology – Stay competitive with modern welding equipment
  • Ownership options – Buy the equipment, upgrade, or return it at the end of the lease

You also have the option to purchase your equipment early, including within the first 12 months.

Tax Advantages

In many cases, lease payments for business-use equipment may be tax-deductible. This can reduce your overall cost and free up capital for additional tools, supplies, or labor.

(Consult your tax advisor for details.)

Apply in Minutes

Financing is available 24/7, so you can apply whenever it’s convenient.

  • Application takes about 4 minutes
  • Instant decision in most cases
  • Immediate access to eDocs
  • Order your equipment right away

If approved for more than your initial request, you can easily adjust your financing to include additional items.

Need Help?

Have questions about financing or lease-to-own options?

Contact the WeldingMart team — we’re here to help you find the right solution for your business. 877-532-9353.

 
WEARSHIELD® 60 stick electrode is ideal for extreme abrasion hardfacing applications such as conveyor screws, brick and coke machinery, grader blades and crusher rolls/plates/jaws (Metal-to-Earth (Earth Cutting & Digging) for Extreme Abrasion and Low to Moderate Impact)
Overview

WEARSHIELD® 60 stick electrode is ideal for extreme abrasion hardfacing applications but is limited to two layers. Typical applications include conveyor screws, brick and coke machinery, grader blades and crusher rolls/plates/jaws. It can be welded in flat & horizontal positions.

Features
  • Designed to resist severe abrasion
  • It exhibits higher alloy and higher abrasion resistance than Wearshield® ABR, Wearshield® 44 or Wearshield® ME
  • Can be used on carbon, low alloy, stainless, and manganese steels
  • Deposits consist of primary carbides in a matrix of austenite-carbide eutectic
  • Deposits should be limited to two layers

Specifications
FeatureValue
Classification Number of layerHardness Rockwell C
Typical Result 1 Layer57-60
Typical Result 2 Layers60-62
Classification Number of layer%C%Cr%Mn%Mo%Si%V
Typical Result 2 Layers5.023.00.82.31.00.6
Diameter Polarity⁽¹⁾Current, Amps
1/8 in (3.2 mm) DC+100 - 140
1/8 in (3.2 mm) AC110 - 150
5/32 in (4.0 mm) DC+130 - 180
5/32 in (4.0 mm) AC140 - 200
3/16 in (4.8 mm) DC+210 - 250
3/16 in (4.8 mm) AC230 - 270
Note
⁽¹⁾ Preferred polarity is listed first.
NOTE: The deposit is not machinable or forgeable. Cooling rate does not significantly influence abrasion resistance. Deposit will usually cross check.
If more than two-layer build-up is required, use Wearshield® 15CrMn (preferred), Wearshield® BU or Wearshield® BU30 for the preliminary layer or layers under Wearshield® 60.
On manganese steel, use Wearshield® Mangjet® or Wearshield® 15CrMn as build-up.
Preheat is not generally necessary except to be sure that work is in room temperature range 25° - 45°C (75° - 100°F).
However, preheat of 120° - 200°C (250° - 400°F) may be necessary to prevent heat affected zone cracking on high carbon steel or low alloy steel base metals.
If more than two layers must be used, or if cross checks must be eliminated, preheat to 650°C (1200°F).
Prolonged or repeated heating of manganese steel base metal over 260°C (500°F) can cause embrittlement and spalling.
Avoid base metal embrittlement by: • Limiting the temperature 260°C (500°F) at distances of 13 mm (1/2 in) away from the weld. • Minimizing the time at elevated temperatures.
The correct welding technique is a vertical electrode with a 3.2 - 4.8 mm (1/8 - 3/16 in) arc length. The large ball on the end of the electrode should never touch the puddle. This technique will give a smooth transfer, low spatter and smooth bead.
LECO Diameter 1/8 x 14 in (3.2 x 350 mm)
LECO Package (4) 10 lb Plastic Tube
Diameter (in) 1/8
Length (in) 14