Proper joint preparation is critical for sound brazed joints: clean all joint surfaces to remove oil, oxide, and scale using emery cloth or a wire brush. Maintain proper joint clearance for capillary flow. Heat the base metal — not the filler rod — to brazing temperature before touching the rod to the joint. The heat-to-flow sequence ensures proper capillary action. Allow the joint to air cool before quenching to avoid thermal shock cracking.

Harris 45F6184 - Safety-Silv 45FC Flux-Coated Silver Brazing Alloy - 1/8 in (3.2 mm) - 4 oz Tube

Q: What is the Harris 45F6184 - Safety-Silv 45FC Flux-Coated Silver Brazing Alloy - 1/8 in (3.2 mm) - 4 oz Tube used for?

The Harris 45F6184 - Safety-Silv 45FC Flux-Coated Silver Brazing Alloy - 1/8 in (3.2 mm) - 4 oz Tube is a silver brazing alloy (Safety-Silv 45). Silver brazing alloys produce strong, ductile joints on ferrous metals, copper, copper alloys, and many dissimilar metal combinations. They flow at lower temperatures than conventional copper-phosphorus alloys, reducing base metal distortion. Always use the appropriate brazing flux (Harris Stay-Silv White or Black Flux) with silver brazing alloys.

Q: What diameter is the Harris 45F6184 - Safety-Silv 45FC Flux-Coated Silver Brazing Alloy - 1/8 in (3.2 mm) - 4 oz Tube available in?

The Harris 45F6184 - Safety-Silv 45FC Flux-Coated Silver Brazing Alloy - 1/8 in (3.2 mm) - 4 oz Tube is available in 1/8 diameter. Rod or wire diameter selection depends on joint gap clearance and feeding method: narrow-gap joints with tight clearances benefit from thinner rod (easier to feed into the joint), while larger-gap joints require more filler and may work better with thicker rod. Pre-placed rings or preforms are available for production brazing of consistent joint geometries.

Q: Does the Harris 45F6184 - Safety-Silv 45FC Flux-Coated Silver Brazing Alloy - 1/8 in (3.2 mm) - 4 oz Tube require brazing flux?

Silver brazing alloys require a compatible brazing flux to prevent oxidation during heating and to aid flow. Harris Stay-Silv White Flux is recommended for most silver brazing applications at brazing temperatures up to approximately 1600°F. For higher-temperature alloys or extended-cycle brazing, Stay-Silv Black Flux handles temperatures up to approximately 1800°F. Apply flux to all base metal surfaces before heating.

Q: What package size is the Harris 45F6184 - Safety-Silv 45FC Flux-Coated Silver Brazing Alloy - 1/8 in (3.2 mm) - 4 oz Tube available in, and how should I store it?

Brazing alloys are sold in various rod lengths and weights — common sizes include 1 lb, 5 lb, and 25 lb packages. Store in a dry location free from oil and solvent contamination. Silver brazing alloys are stable at room temperature and do not require special controlled-atmosphere storage. Keep surfaces clean to ensure proper flux adhesion and capillary flow.

SKU: 45F6184

$343.41

Factory Direct

Free Shipping

Lowest Price

Safety-Silv 45FC Flux-Coated Silver Brazing Alloy - 1/8 in (3.2 mm) - 4 oz Tube

Overview

Safety-Silv 45 flux-coated high silver brazing alloy performs like a 45% silver cadmium-bearing alloy, but is cadmium-free. The flux coating on the wire eliminates the need for manual flux application. It has a lower melting temperature than Safety-Silv 45. Its excellent fillet-forming quality produces high-strength ductile joints. Certified to NSF Standard 51.

Features

General purpose cadmium-free silver brazing alloy
Excellent joint strength and ductility at moderately higher temperature with a melting range of approximately 145 degrees F (63 degrees C)
Good ductility and capillary flow
Fillet forming qualities are suitable for filling loose connections
Recommended joint clearance of 0.003 in. - 0.006 in. (0.08 mm - 0.15 mm)
Popular choice to braze copper, brass, steel and Stainless Steel
Flux-coating eliminates the need for manual flux application
ANSI/AWS A5.8 ASME SFA 5.8, QQ-B-654A Class BAg-5, ISO 17672 Ag 245
One year warranty

Reviews

Q&A

Product Overview

Features

General purpose cadmium-free silver brazing alloy
Excellent joint strength and ductility at moderately higher temperature with a melting range of approximately 145 degrees F (63 degrees C)
Good ductility and capillary flow
Fillet forming qualities are suitable for filling loose connections
Recommended joint clearance of 0.003 in. - 0.006 in. (0.08 mm - 0.15 mm)
Popular choice to braze copper, brass, steel and Stainless Steel
Flux-coating eliminates the need for manual flux application
ANSI/AWS A5.8 ASME SFA 5.8, QQ-B-654A Class BAg-5, ISO 17672 Ag 245
One year warranty

Harris 45F6184 - Safety-Silv 45FC Flux-Coated Silver Brazing Alloy - 1/8 in (3.2 mm) - 4 oz Tube

Product Overview

Features

Product Reviews

Questions & Answers