What is the Harris STAY SILV POWDER FLUX 1/4# JAR - SSPF1/4 used for?

The Harris STAY SILV POWDER FLUX 1/4# JAR - SSPF1/4 is used to prevent oxidation of base metal and filler metal surfaces during welding, brazing, or soldering operations. Flux chemically cleans metal oxides during heating and promotes proper bonding between the filler and base metals. Select flux based on the process (soldering, brazing, or welding) and base metal type.

What applications and base metals is the Harris STAY SILV POWDER FLUX 1/4# JAR - SSPF1/4 suitable for?

Flux type must be matched to the process temperature and base metal: soldering fluxes activate at low temperatures (below 450°C), brazing fluxes work in the 450–1100°C range, and SAW welding fluxes handle arc temperatures above 1500°C. Never substitute flux types across different temperature ranges.

How do I apply the Harris STAY SILV POWDER FLUX 1/4# JAR - SSPF1/4 correctly?

Apply flux using an appropriate method for the process: brush application for soldering and brazing fluxes (cover all joint surfaces evenly), pre-placed granular flux feeding for SAW welding. Flux quantity matters — too little flux leaves bare areas that oxidize; too much flux can be difficult to remove after welding or brazing. Apply a thin, even coat to all contact surfaces.

How do I remove flux residue after using the Harris STAY SILV POWDER FLUX 1/4# JAR - SSPF1/4?

All flux residue must be removed after completing the joint. For brazing and soldering, clean flux residue with warm water and a stiff brush immediately after the joint cools — flux becomes harder to remove as it ages. For SAW welding, remove slag and flux residue with a chipping hammer and wire brush between passes and after final welding. Confirm complete flux removal, especially in pressure vessel, pipe, and food-grade applications where residue can cause corrosion or contamination.

How should I store the Harris STAY SILV POWDER FLUX 1/4# JAR - SSPF1/4?

Store flux in a sealed container in a cool, dry location. Moisture contamination degrades paste and powder fluxes — activated flux or flux that has absorbed moisture should be discarded and not used, as it can cause porosity or incomplete flux activation during the joining operation. Keep containers sealed between uses.

Harris STAY SILV POWDER FLUX 1/4# JAR - SSPF1/4

SKU: SSPF1/4

$175.00

Factory Direct

Free Shipping over $250

Lowest Price

STAY SILV®WHITE POWDER BRAZING FLUX

AWS / Classification: (AWS), A5.31 Class FB3-F

Overview

Harris STAY SILV POWDER FLUX 1/4# JAR - SSPF1/4

Powder brazing flux designed for torch brazing most ferrous and non-ferrous base metals, including copper, brass, bronze, steel, Stainless Steel, and nickel alloys. It is not recommended for aluminum, magnesium, titanium, or aluminum bronze. Stay Silv White Powder flux is formulated for use with American Welding Society, (AWS), BAg and BCuP filler metal classifications.

ACTIVATION RANGE: 1050 – 1600°F (566 - 871°C)

Reviews

Q&A

Product Overview